Optimisation Of Sintered Glass Ceramics From An Industrial Waste Glass

Sintered glass ceramic samples of optimized composition glass clay waste weight proportion equal to 50 30 20 featured a water absorption below 2 a good specific strength and above all a substantially unchanged f content compared to the starting mixture.

Optimisation of sintered glass ceramics from an industrial waste glass.

Recent papers have shown that sinter crystallisation is a very effective process for obtaining strong and dense glass ceramics from waste glasses i e. Glasses from the melting of several kinds of industrial waste the technology relies on the viscous flow sintering of fine glass powders with concurrent crystallisation in turn due to a surface mechanism. The measured microhardness of this material was of 5 3 0 04 gpa which is a similar value of other waste derived glass ceramics. Request pdf optimisation of sintered glass ceramics from an industrial waste glass industrial plasma melting of municipal solid waste msw incinerator fly ashes leads to a glass that may be.

Two step thermal process. 28 figure 5a shows the typical. Synthesis of an original glass composition with specific sinter. 20 28 in addition the coefficient of thermal expansion 9 5 10 6 c 1 is also comparable to the ones already measured in waste derived glass ceramic materials.

The sintered materials exhibit a well developed and reproducible glass ceramic microstructure comprising a silicate matrix with dispersed crystalline phases. Enrico bernardo giovanni scarinci erika edme ulysse michon nicholas planty fast sintered gehlenite glass ceramics from plasma vitrified municipal solid waste incinerator fly ashes journal of the american ceramic society 10 1111 j 1551 2916 2008 02892 x 92 2 528 530 2009. The hazardous industrial waste used may range from 50 to 70 percent of the raw material used which is higher in comparison to other similar technologies. Industrial plasma melting of municipal solid waste msw incinerator fly ashes leads to a glass that may be easily crystallised to gehlenite glass ceramics by the sintering of fine glass powders.

The technology of granite like glass ceramics from hazardous industrial wastes is based on the following steps. The production of glass ceramic materials based on inorganic industrial waste generated by different industries is a promising line and has been used very successfully to crystallize important ceramics from the glass phase.